New Delhi, Jan 28 (.) A high-voltage supercapacitor based on a dual-functional Porous Graphene Carbon Nanocomposite (PGCN) electrode has been developed, which could facilitate stabler supercapacitors for applications like solar panels and also provide electric vehicles with increased range and faster acceleration, said the Ministry of Science & Technology in a statement on Wednesday.
Conventional electrolytes used in commercial supercapacitors can operate between 2.5–3.0 V and begin to decompose or face safety issues (such as flammability) at higher voltages.
This innovation addresses electrolyte instability, doubling energy density to provide electric vehicles with increased range and faster acceleration while simplifying module design through reduced cell stacking, the ministry said.
Researchers at the International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), an autonomous institute of the Department of Science and Technology (DST), used dual-functional PGCN electrodes to reach an unprecedented 3.4 V, overcoming the 3.0 V limitation of conventional supercapacitors, along with significantly improved energy storage.
The enhanced performance originates from the engineered surface of the PGCN material, which is both water-repellent and highly compatible with organic electrolytes.
This dual functionality suppresses water-induced degradation and enables rapid electrolyte penetration into the porous structure, improving ion transport and electrochemical efficiency.
As a result, the supercapacitor delivers 33 percent higher energy storage, high power output, and excellent long-term stability, making it suitable for electric vehicles, grid-scale storage, and portable electronics.
As per the information shared by the Ministry of Science & Technology, PGCN electrodes are produced through an eco-friendly hydrothermal carbonization process using 1,2-propanediol as the precursor.
Conducted at 300 degrees Celsius for 25 hours in a sealed vessel, the process eliminates the use of harsh chemicals and external gases, minimizes environmental impact, achieves yields exceeding 20 percent, and is scalable from laboratory to industrial production.
The resulting material exhibits a micro- and mesoporous architecture that supports rapid ion transport and high energy storage, delivering a power density of up to 17,000 W/kg.
Consistent performance is ensured through precise control of synthesis parameters. Compared with commercial carbon-based electrodes, the PGCN electrode simultaneously enhances operating voltage and power output.
PGCN-based supercapacitor stores 33 per cent more energy than conventional devices and retains 96 per cent of its performance after 15,000 charge/discharge cycles, demonstrating exceptional durability, as shown below.
. VK VAN RB 1648